Description:
1.Advanced technology2.functional bending strength
3.blanks for full-arch dental restorations
4.100% biocompatibility
dental zirconia ceramic block for other dental cadcam system
Mainfeature:
- Select the best raw materials
- After dry pressed and cold isostatic: balanced pressure, betterstrength: better color: more translucent
- More accurate scaling factor (the persistent and consistency ofscaling factor between each batch)
- Reliable, controllable, reusable production process to make sureproduce the products with the same quality.
- Easy to cut, no porcelain breakage, less scraps
- Every block has its barcode easy to control lot size, and itincluding information such as scaling factor.
Ouradvantage:
- Perfect fit
- Stable scaling factor
- Imagination permeability coloring, not only stay onsurface
- Strength and translucent better than any other similarproducts.
- Operate fastly, save cutting knives.
- Professional service and supporting
- Senior R&D team ensure the continued excellence of ourmaterial.
technicalparameter
Colour | White(light colored)and uniform, thin-wall issemitransparent |
Sinteringdensity (densely sintered in hightemperature) | (6.05±0.03) g/cm3 |
Chemicalcompositions | ZrO2 HfO2 Y2O3>99.0wt% Al2O3<O.5 wt% Other oxides<O.5 wt% |
Bendingstrength | ≥900MPa |
Chemicalsolubility | 6.7µg·cm-2 |
Radioactivity | 0.0024Bq/g |
cytotoxicity | The grade of the cytotoxicity is 0 |
Short term systemic toxicity test–oral route | Has no systemic toxicity |
Delayed-typehypersensitivity | Has no sensitization |
Hemolysis | Hemolysis is 0 |
We choose thebest zirconia powder and utilize a cold isostatic pressing systemto form shapes; the main advantage of isostatic pressing is theuniform application of pressure, which leads to a very homogeneousdensity and shrinkage, yielding a very reproducible process. Theproduction cost by using isostatic pressing is much higher thanuniaxel dry pressing, but quality is also much higher. We try toprovide high quality, low cost zirconia blocks for all dentalCAD/CAM milling system, support open architecture CAD/CAM millingsystem.
upceracompatible dental zirconia block
P/N | specification | L*W*H(mm) |
WT10 | 98-10 | 98*10 |
WT12 | 98-12 | 98*12 |
WT14 | 98-14 | 98*14 |
WT16 | 98-16 | 98*16 |
WT18 | 98-18 | 98*18 |
WT20 | 98-20 | 98*20 |
WT22 | 98-22 | 98*22 |
WT25 | 98-25 | 98*25 |
HT&STavailable, HT&ST all made outof Tosho powder fromJapan | ||
Wesincerely welcome you to try this material and introduce thisexcellent quality to your clients and patients!