Description:
conditioned cut wire shotsize: 0.2 to 1.5, other size can be customized
SGS certification
Good quality
for shot blasting
| Low carbon steel shot/mild carbon steel shot | |||||||
| commodity | size available | symbol | chemical | density | hardness | picture | |
| (mm) | of material | composition | (g/cm³) | ||||
| low carbon wire shot/mild carbon wire shot | 0.2mm, 0.3mm, 0.4mm, 0.5mm, 0.6mm, 0.7mm, 0.8mm, 1.0mm, 1.2mm, 1.5mm | low carbon wire Q195 | C:0.06-0.12% Mn:0.25-0.5% Si≤ 0.3% S≤0.05% P≤0.45% | 7.84g/cucm | 30-40HRC | ||
| C:0.1 Mn:0.4% Si:0.1% | 40-50HRC | ||||||
our company have 15years experience to produce thisproduct..
we adopt the best steel wire to cut and produce.
1.As cylindrical cut wire is produced by cold drawn steel wire,it is absolutely free from micro structural defects, like presenceof hyper entectole carbides and porosity
2.The cut wire size is stabilized due to the drawing processcontrol
3.Equal hardness and excellent homogeneity because of highquality of raw materials and quality control methods
4.Higher durability compare to cast steel shots; steel cut wireshot is four to five times as efficient as steel shot
5.The components peened with conditioned cut wire shots have agreater fatigue life than the same components peened with caststeel shots
6.Less dust during operation contribute to a better workenviroment
7.Obviously effet on surface of parts, very bright and clean
8.Low wastage during operation
9.High strength and non-friable, used by a wide range ofmachinery, chemical equipment, vessel, container, lightmanufacturing and so on