Description:
175 degree heat shrink tube1.made from high tem PVDF materials
2. outstanding abrasion and cut-through resistance
Description
LK-175 is semi-rigid, excellent flame retardant heat-shrinkable Polyvinylidene fluoride(PVDF) tube for applications requiring high temperature performance, outstanding abrasion and cut through resistanceor superior chemical and solvent resistant properties.
It reliably protects wires, solder joints, terminals andconnections and components from most industrial fuels, solvents andchemicals.
Features
>Approvals: UL, VW -1
>Meet: RoHS, SAE-AMS-DTL-23053/18
>Operating temperature: -55°C to 175°C
>Minimum shrink temperature: 175°C
>Standard color: Clear
Property | Test Method | Typical Data |
Operating temperature | IEC 216 | -55°C to 175°C |
Tensile strength | ASTM D 2671 | 34.5MPa |
Elongation at break | ASTM D 2671 | 150% |
Elongation at break after aging | 250°C/168hrs. | 100% |
Heat shock | 300°C/1hr. | No cracking |
Cold bend | -55°C/1hr. | No cracking |
Flammability | VW -1 | Pass |
Volume resistance | IEC 93 | 1013Ω.cm |
Dielectric strength | ASTM D 2671 | 30kV/mm |
Normalsize | As supplied(mm) | After recovered (mm) |
Standard length | ||
(inch) | (mm) | Inside diameter (Min.) | Inside diameter (Max.) | Wall thickness (Nom.) | |
3/ 64 | 1.2 | 1.2 | 0.6 | 0.20 | 200m/spool |
1/16 | 1.6 | 1.6 | 0.8 | 0.20 | 200m/spool |
3/ 32 | 2.4 | 2.4 | 1.2 | 0.23 | 200m/spool |
1/ 8 | 3.2 | 3.2 | 1.6 | 0.23 | 100m/spool |
3/16 | 4.8 | 4.8 | 2.4 | 0.23 | 100m/spool |
1/ 4 | 6.4 | 6.4 | 3.2 | 0.28 | 100m/spool |
3/ 8 | 9.5 | 9.5 | 4.8 | 0.28 | 1.22m |
1/ 2 | 12.7 | 12.7 | 6.4 | 0.32 | 1.22m |
3/ 4 | 19.1 | 19.1 | 9.5 | 0.36 | 1.22m |
1 | 25.4 | 25.4 | 12.7 | 0.41 | 1.22m |