Description:
1.Hydraulic hose assembly(any types);2.DOT Certificate, SAE J1401 & FMVSS 106 Standard;
3.30days delivery
4.ISO/TS16949
JL has formed the catalogs of hydraulic brake hose assemblies with OEM No(3000types), which are used for OEM and aftermarket for any vehicles; Designing and researching hose assemblies according to
customers’requirements and international safe standards; Tested 100% against SAE J1401 before shipment.
Features:
Pressure test | No leakage in 2 min under pressure of 19.6±0.48 Mpa |
Volumetric expansion | Less than 0.68cm3/m under 6.9Mpa; less than 0.79cm3/m under 10.3Mpa |
Burst test | No leakage more than 60 Mpa |
Low temperature | No visible crack without magnification within 72 hr under -55°C |
Whip test | No damage after 35 hrs’ rotating at 800rpm |
Tensile test | No breakage or rupture with 2310 N tensile stress |
Ozone test | No cracks when examined under 7X magnification under 50°C in 50Mpa±5Mpa |
Water absorption test | No leakage under 60 Mpa; no damage within 50hrs; no breakage or rupture with 2080 N tensile stress |
Guaranteed for | 100000kms or 5years |
| TEST PERFORMANCE | |||||||||
| Product Name | HYDRAULIC BRAKE HOSE 1/8" (3.2x10.5mm)SAE J1401 | ||||||||
| No | Test Item | QTY | SAE J1401 Standard specification | Test Result | |||||
| 1 | Volumetric Expansion | 4 | 6.9Mpa | HR | HL | 0.45 | 0.46 | 0.45 | 0.45 |
| 2.17 | 1.08 | ||||||||
| 10.3Mpa | 2.59 | 1.38 | 0.65 | 0.65 | 0.66 | 0.65 | |||
| 2 | Burst Test | 4 | ≥49.03Mpa | 62 | 62 | 63 | 62 | ||
| No Leakage No Blowing Off | |||||||||
| 3 | Brake Fluid | 4 | 27.6Mpa Hold 2M | ≥φ2.03mm | OK | OK | OK | OK | |
| Compatibility | Burst≥34.5Mpa | 80up | 80up | 80up | 80up | ||||
| 4 | Whip Test | 4 | ≥35H, 1.55-1.72 Mpa, 800rpm±10rpm. No pressurereduction | 51 | 51 | 52 | 50 | ||
| No water leakage | ND | ND | ND | ND | |||||
| 5 | Tensile Test | 4 | ≥1446N | 2300 | 2300 | 2300 | 2300 | ||
| DN | DN | DN | DN | ||||||
| 6 | Cold Bend Test | 1 | -45- -48°C 70-72H, bend to 180°around mandrel for3-5s | -55°C, nocracks | |||||
| No cracks or breaks (Visible withoutmagnification) | |||||||||
| 7 | Ozone Test | 1 | 100mpa±5mpa, 40 3°C for 70-72H | OK | |||||
| No cracking under 7X Magnification. | |||||||||
| 8 | Salt Spray Test | 1 | 5 parts±1 part by weight of sodium chloride to 95 partsof distilled water. Ato Mization at 35°C, subject the ass''y to thesalt spray for 24H, No base metal Corrosion. | >80h | |||||