Brand:Zhongya
MOQ:1
Quantity:500
Product Feature
l Good processperformance and low fuzz
l Compatibilitywith multiple of resin systems
l Complete andfast wet-out
l Goodmechanical properties
l Excellent acidcorrosion resistance
Identification
Technical Parameters
Linear Density(%) | Moisture Content (%) | Size Content (%) | Breakage Strength(N/tex) |
ISO 1889 | ISO 3344 | ISO 1887 | ISO 3341 |
/-5 | <=0.10 | 0.55 /-0.15 | >=0.40 |
Mechanical Properties
Mechanical Properties | Unit | Value | Resin | Method |
Tensile Strength | MPa | 2741 | UP | ASTM D2343 |
Tensile Modulus | MPa | 81232 | UP | ASTM D2343 |
Tensile Strength | MPa | 2673 | EP | ASTM D2343 |
Tensile Modulus | MPa | 81126 | EP | ASTM D2343 |
Shear strength | MPa | 70 | Epoxy | ASTM D2344 |
Shear strength retention (72 hr boiling) | % | 94 | epoxy |
|
Storage
Unless otherwise specified,the fiberglass products should bestorde in a dry ,cool and moisture-proof area. The room temperatureand humidity should be always maintained at 15C~35C and 35%~65%.Itis best if the product is used within 12months after productiondate .The fiberglass products should remain in their originalpackaging until just prior to user.
To ensure safety and avoid damage to the product, the palletsshould not be stacked more than three layers high. When the palletsare stacked in 2 or 3 layers, special care should be taken tocorrectly and smoothly move the top pallet
Packaging
The product can be packed on pallet or in small cardboardboxes.
Package height mm (in) | 260 (10) | 260(10) |
Package inside diameter mm (in) | 160(6.3) | 160(6.3) |
Package outside diameter mm (in) | 275(10.6) | 310(12.2) |
Package weight kg (lb) | 15.6(34.4) | 22(48.5) |
Number of layers | 3 | 4 | 3 | 4 |
Number of doffs per layer | 16 | 12 | ||
Number of doffs per pallet | 48 | 64 | 36 | 48 |
Net weight per pallet kg(in) | 750(1653.4) | 1000(2204.6) | 792(1746) | 1056(2328) |
Pallet length mm(in) | 1120(44) | 1270(50) | ||
Pallet width mm(in) | 1120(44) | 960(37.8) | ||
Pallet height mm(in) | 940(37) | 1180(45 | 940(37) | 1180(46.5) |