PHZA bead-grind media

Name: Aluminum Composite ball ZTA Zirconium
Category: Aluminum Composite zirconium ball
Technology: Sintering
Size :0.2-20mm
Density: In accordance with the content ofzirconium to determine
Accumulation of proportion: In accordance with thezirconium content, the more the more serious
Hardness: 800HV1

Strength, and aluminum zirconium as the perfect combination ofgrain, excellent wear resistance, especially for use in coatings,inks, agricultural chemical, mineral pigment grinding anddispersion. Applicable to the majority of sandingmachine. 

 

Features :
Zirconia Toughened Alumina (ZTA) is a set mill referred superwear-resistant zirconium oxide, high toughness, high-density andhigh hardness alumina, corrosion resistance and othercharacteristics of the new products as a whole. Modest price of theproduct, the right density, excellent wear resistance.

The application of occasions :
Non-metallic mineral, paint, ink, paper, coatings, electronicmaterials, magnetic materials, dyes, food, medicine, etc.

 

PerformanceIndex:

 

Compassion	wt%	20~80% ZrO2 80~20% A2O3
Packed Density	Kg/L	2.6~3.3(Φ7mm)
Specific Density	g/cm3	4.1~5.5
Hardness(HV)	GPa	>8.5
Elastic modulus	GPa	200
Thermal Conductivity	W/m.K	3
Crushing Load	KN	≥8 (Φ7mm)
Fracture Toughness	MPam1-2	6.7
Grain size	µm	≤0.8
Thermal expansion Coeffcient(20-400 )°C)	10x10 -6 / °C(20-400)	7.0

Content:  

ZrO2	50%
AL203	50%

 

 

 

10~15mm Aluminum Composite ball ZTA Zirconium