ORACLE S CR30 BK is carbon fibrereinforced polyamide 66 resin
high strength,rigidy and stiff
electrically conductive nylon
it dilivers higher wear resistant properties
| TEST ITEMS | TEST METHOD AND CONDITIONS | ||
| TEST METHOD | UNIT | CONTITIONS | |
| (DRY)23 | |||
| Density | ISO1183 | g/cm3 | |
| Melt Volume Rate | ISO1133 | cc/10min | (275)2.16kg |
| Tensile Strength | ISO527 | MPa | 10mm/min |
| Tensile strain at break | ISO527 | % | |
| Flexural Strength | ISO178 | MPa | |
| Flexural Modulus | ISO178 | MPa | |
| Charpy Notched | ISO179 | KJ/m2 | 2.9m/s-1J |
| Izod Notched Impact | ISO180 | KJ/m2 | 3.5m/s-1J |
| Flame resistance | UL-94 | ||
| Ash content | % | ||
| Processing Guidelines | |||
| Material Handling Max. Water content: 0.12% Product is supplied in sealed containers and drying prior tomolding is not required. If drying becomes necessary, adehumidifying or desiccant dryer operating at 80 °C (176 °F) isrecommended. Drying time is dependent on moisture level, but 4-6hours is generally sufficient | |||
| Typical Profile Melt Temperature 270-305 °C (518-581 °F) Mold Temperature 70-90 °C (158-194 °F) Injection and Packing Pressure 35-125 bar (500-1500psi) | |||
| Fill Rate Fast fill rates are recommended to ensure uniform melt delivery tothe cavity and prevent premature freezing. Surface appearance isdirectly affected by injection rate | |||
We direct our energies to offer users the high-performance,consistent-quality ,cost-savingnylon. Each batch have to pass stricttest before they go out .
ORACLE provide six series polyamides resin to serveusers a wide range of needs.
>>> General PurposeHomopolymer
>>> Reinforced nylonresin(Glass-reinforced and/or Mineral-reinforced)
>>> Flame Retarded
>>> Friction&Wearresistance
>>> Impact resistance
>>> Special applications
Contact us for further information,general guides and/or additional information aboutventilation