Brand:Shangjiu
MOQ:1
Quantity:15
Biodegradable Plastic Resin
Model Number: BOR-Z-501F
Product Type: starch based biodegradable resin for film andbags
Product Features: Absorb moisture easily, can be decomposed bymicrobes easily, anti-static, the processing temperature is lower5-10 celsius degrees than conventional plastics, can be easilycolored. Such resin can be processed into finish products, withoutadding any other polyolefin materials, like PE, PP, PVA, EVA,etc.
Products Testing:
1) compliance with ISO14855:1999
2) the degradation rate is more than 46% in 100 days.
3) test report from China National Center for QualitySupervision and Test of Plastics Products can be provided.
Property data:
BOR-Z–501F | |||
Testing Item | Standard | Unit | Result |
Appearance | Q/320113SSD001 - 2002 |
| Light Yellow |
Density | GB 1033 | g/ cm3 | 0.98 – 1.10 |
Moisture Content | Q/320113SSD001 - 2002 | % | 0.3 – 1.2 |
Melt Flow Index | GB3682 | g/10 min | 0 - 2 |
Tensile strength | GB 1040 | MPa | ≥12 |
Breaking Elongation | GB 1040 | % | ≥250 |
Bio Substances Content | Q/320113SSSD001 - 2002 | % | ≥55 |
n-hexane Extracts | GB/T5009.58 | % | ≤4.0 |
Softening Point | GB/1633 | ºC | > 65 |
Degradation rate in100days | ISO14855:2000 | % | > 46 |
The data for tensile strength and elongationrefer to that of finished film products. | |||
Recommanded Applications:
For all sorts of anti-static packing purpose, like electronicproduct packaging, car interior covering film, electrical appliancepackaging, agricultural mulch film, shopping bags, T-shirt bags,filter bags, storage bags, bin bags, tear-on-roll bags, disposablegloves, table cloths, aprons and raincoats, etc.
Processing Equipment:
Common film blowing extruder, sheet extruder, bags makingmachine, printers, and heat sealing machines are all can beused.
Processing Technology:
1) Best results will be achieved with a screw L/D ratio ≥ 28:1.The blow-up ratio should be more than
1:3 to achieve the maximum production yieldand the best quality.
2) BOR-Z-501F can be blended with LDPE to process filmproducts.
3) Newly made film feels brittle or crispy. Its elongation islow. This is due to severe dehydration during production.Therefore, the film needs to be settled for a 24- hour curingperiod to regain elongation and anti-tear strength before beingused to make finish products, e.g. bag-making or printing.
4) The minimum thickness of film made of such material can be 10microns.
Biodegradable corn starch basedplastic resin