Properties

Testing method 

Unit 

Hot melt grade

EVA 28

 EVA18      

MFI 

ASTM D1238

g/10min

150.0

 190

VA content 

HPC

Wt%

28

 18

Density 

ASTM1505

g/cm3

0.951

 0.948

Melting point 

HPC

°C

67

Soften point 

ASTM1525

°C

 40 max

Ultimate tensil strength

ASTM238

g/cm3

-

Breaking elongation

HPC

Wt%

-

hardness

ASTM2240

g/cm3

 21

Tensile modulus

HPC

°C

 -

Volume resistivity

D257

Ω.cm