Product Introduction
CY-01 two component polysulfide sealant is solvent free, roomcuring, polysulfide type sealant, which has excellent cohesion andairproof performance, especially research for manufactureenvironmental and energy-saving insulating glass component, it’smainly suitable for the product line of insulating glass,polysulfide sealant contain thixotropic polysulfide base (Acomponent) and curing agent (B componet). If mix this sealantaccording to rated proportion, this sealant could adhere to glass,aluminum product etc material, and without beforehanddaubing.Product Characteristics
Solvent free: don’t produce any volatile compound. Outstandingthixotropism, suitable for all-wave construction.
Low tack: construction craftwork is simple and improve efficiency,cost reduction. After solidification, it form elastomer???which hasexcellent cohesion to glass and aluminum alloy etc metal.
Suitable for all kinds of climate: it could keep itscharacteristics from -50??? to 100??? and could construct from-5??? to 45???. It has compatibility with all kinds of hot meltbutyl, suitable for the manufacture of double times sealing ofinsulating glass.The Main Technology
The following data only for reference only.
| No | Item | Technical data | ||
| 1 | Appearance | A component | White paste | |
| B component | Black paste | |||
| 2 | Pulling and bond strength(Mpa) 72h | ≥0.6 | ||
| 3 | Suitable period min???S | ≤10 | ||
| 4 | Surface dry time | ≤2 | ||
| 5 | slump | vertical placement | ≤1 | |
| horizontal placement | No distortion | |||
| 6 | hardness???A??? 24h | 20-40 | ||
| Note: the above experiment condition is 24±0???2???, mix proportion A:B =10:1 | ||||
It must make bonding material compatibility test before use, itcould be construct after confirm the product and base materialconform to the construction requirement.
Mix proportion: A,B component matching range: 10:1,curing speed canalso be controlled through adjusted proportion. ( with more Bcomponent, the curing time is shorter; with less B component, thecuring time is longer), mixing ratio should be uniformity and nocolor variation.Product Package:
330kg metal barrel: A component:300kg/barrel B component:30kg/barrel
38kg barrel: A component:34.5kg/barrel B component:3.5kg/barrel
33kg carton: A component: 30kg Bcomponent: 3kg (6 pieces in one carton) (note: it could bepacked according to customer’s requirement)Storage Life
Please keep in cool and dry place below 27??? to extend thevalidity of product, the validity period is 12 months.Mode of Transportation
This product is nonflammable, nonexplosive, non-toxicity, it couldtransport by train, vehicle, ship, airplane etc.Serious Statement: this product cannot be used as structuralcohesiveness of curtain wall, sunroof, sun room, frostedglass