high temperature alloy hollow steel pipe Inconel 600, 800
Inconel 600 is our representive brands.We can provide various specifications, and can also Produce according to your specific requirements
Inconel 600 is a nickel-chromium alloy with good oxidation resistance at high temperatures and resistance to chloride ion stress-corrosion cracking, corrosion by high-purity water, and caustic corrosion. Used for furnace components, in chemical and food processing, in nuclear engineering, and for sparking electrodes.
Typical analysis in percent
C | MN | S | Si | Cr | Ni | Cu | Fe |
0 .15 max | 1.0 max | 0.015 max | 0.5 max | 14.0 -17.0 | 72.0 min | 0 .5 max | 6.0 - 10.0 |
Physical properties
Density: 8.4g/cm3
Melting point/range: 1355-1413°C
Typical mechanical properties(At room temperature)
Ultimate tensile strength(mpa) | Yield strength(mpa) | Elongation in 50 mm(%) |
655 | 310 | 40 |
Incoloy 800 alloy can be forged, hot-upset and impact extruded. Although the alloy tends to work-harden, you can have Hastelloy successfully spun, deep-drawn, press formed or punched.
Standards: ASME SB-407; ASME SB-829; ASME SB-514; ASME SB-775
Typical analysis in percent
Alloy | C | Cr | Ni | Ti | Al | Fe | Al + Ti | Grain |
800 | 0.10max | 19.0 - 23.0 | 30.0 - 35.0 | 0.15-0.60 | 0.15 - 0.60 | 39.5min | 0.30 - 1.20 | Not specified |
800H | 0 .05 - 0.10 | 19.0 -23.0 | 30.0 - 35.0 | 0.15 - 0.60 | 0.15 - 0.60 | 39.5 min | 0.30-1.20 | 5 or coarser |
800HT | 0.06 -0 .10 | 19.0 -23.0 | 30.0 - 35.0 | 0.25 - 0.60 | 0.25 - 0.60 | 39.5 min | 0.85- 1.20 | 5 or coarser |
Physical properties
Density:8.0g/cm3
Melting range:1350-1400°C
Typical mechanical properties(At room temperature)
Alloy | Ultimate tensile strength(mpa) | Yield strength(mpa) | Elongation in 50 mm(%) |
800 | 500 | 210 | 35 |
800H | 450 | 180 | 35 |