IG-002-01 Flexible Graphite Sheet Pure graphite sheet is made from exfoliated graphite flake and produced through an extensive calendaring process to give a thin flexible foil with no binder or resins,expanding under high temperature and then rolling,It has the characteristics of high temperature resistance,corrosion resistance and good elasticity.
Product Data Sheet:
Temperature: -200~650℃ (In Air)
-200~3000℃ (in non-oxidizing media)
Density: 1.0 g/cm3
Carbon Content: >98%
Sulphur Content:＜1000PPM
Chloride Content: ＜40PPM
Compressibility:≥40%
Recovery: ≥10%
Standard Size and Thickness:
500mm L x 500mm W x 0.2mm~6.0mm T
1000mm L x 1000mm W x 0.2mm~5.0mm T
1500mm L x 1500mm W x 0.2mm~5.0mm T
IG-002-02 Flexible Graphite Roll
Flexible graphite roll is made from exfoliated graphite flake with high carbon content which is gone through chemical treatment,expanding under high temperature and then rolling,It has the characteristics of high temperature resistance,corrosion resistance and good elasticity.
Product Data Sheet:
Temperature: -200~650℃ (In Air)
-200~3000℃ (in non-oxidizing media)
Density: 1.0 g/cm3
Carbon Content: >98%
Sulphur Content:＜1000PPM
Chloride Content: ＜40PPM
Compressibility:≥40%
Recovery: ≥10%
Standard Size and Thickness:
(30m---150m L )x 1000mm W x( 0.2mm~1.0mm) T
(30m L---70m L) x 1500mm W x (0.2mm~1.0mm)T
IG-02-003 Flexible Graphite Tape
This tape was cutted of flexible graphite rolls,Graphite tape filler for spiral wound gasket,In-situ pump and valve gland packing, Manufacture of graphite packing rings,Facing material for camprofile type gaskets,Filler for metal jacketed type gaskets.
Also manufacture Crinkled Graphite Tape.
Length for one roll:50M;80M;100M,120M
Width:4.0MM;5.0MM;5.4MM,5.5MM;5.7MM,6.0MM8.0MM,12MM,14MM Thickness:0.4MM;0.5MM;0.7MM,0.8MM
Test item Test result:
Tolerance of thicknss : ±0.03mm
Tolerance of density : ±0.05g/cm3
Ash content : 0.42%
Carbon content : 99.30%
Tensile strength : 4.5Mpa
Compressibility : 54.73%
Resilience rate : 10.21%
Ignition loss 450°C : <= 1%
600°C : <= 20%
Chlorine content : 30ppm